Determination of bursting resistance of the hottes

Corrugated board burst resistance measurement method

release date: Source: China paper industry

corrugated board system will check the authority of the operator, and a variety of measurement methods are often used. Today, China's paper industry starts with the bursting test method of corrugated board. Let's introduce the use steps of relevant methods

1. Scope

this standard specifies the method of determining the bursting strength of corrugated board by hydraulic pressure increase method

this standard is applicable to corrugated board with a burst resistance of 350-5500kpa

2. Reference standard

the provisions contained in the following standards have their own strengths in Ferrography and spectral analysis, which constitute provisions of this standard through reference in this standard. When this standard is published, the editions shown are valid. All standards will be revised. All parties using this standard should explore the possibility of using the latest versions of the following standards

GB 450-89 paper and paperboard sample taking

GB 10739-89 standard atmosphere for pulp, paper and paperboard sample processing and testing

Motorola in Razr series 3. Definitions

this standard adopts the following definitions

bursting strength

under the test conditions, the uniformly increased maximum pressure that the corrugated board can bear on the unit area perpendicular to the sample surface is the relevant content force to share the solution in case of failure of the tensile testing machine

4. Test principle

place the specimen on the adhesive film, clamp it with the specimen clamp, and then apply pressure evenly to make the specimen bulge freely with the adhesive film until the specimen is broken. The bursting resistance of the specimen is the maximum value of the applied hydraulic pressure

5. Test instrument

5.1 sample chuck system

the diameter of the upper chuck is (31.5 ± 0.5) mm, and the diameter of the lower chuck hole is (31.5 ± 0.5) mm. The upper and lower clamping rings shall be concentric, and the maximum error shall not be greater than 0.25mm. The two clamping rings are parallel to each other and flat. The force on the contact surface is uniform during measurement

in order to prevent the sample from sliding during measurement, the sample chuck should have a clamping force of not less than 690kpa. However, such pressure will generally cause the corrugated collapse of the sample, which should be noted in the report

5.2 adhesive film

the adhesive film is circular and composed of elastic materials. The adhesive film is firmly clamped, and its upper surface is about 5.5mm lower than the top surface of the lower clamping ring. The rubber film material and structure shall make the height of the rubber film protruding from the lower chuck adapt to the elastic resistance, that is, when the protruding height is 10mm, the resistance range is (170-220) kPa; When the projection is 18mm, the resistance range is (250-350) kPa

6. Sample taking and treatment

6.1 the sample shall be taken according to the provisions of GB 450

6.2 the sample shall be treated with warm and wet treatment according to the provisions of GB 10739

7. Preparation of samples

the sample area must be larger than the chuck of the bursting tester, and the sample must not have watermarks, creases or obvious damage. Samples that have been pressed by the chuck shall not be used in the test

8. Test steps

conduct sample cutting and test under the atmospheric conditions specified in article 6.2

open the chuck of the sample, clamp the sample in the middle of the two sample chucks, then start the tester, and gradually increase the pressure at the speed of (170 ± 15) ml/min. When the sample explodes, read the value indicated on the pressure gauge. Then release the chuck and return the reading pointer to the start position. When the sample has obvious sliding, the data shall be discarded

9. Result expression

measure with 10 samples attached to the adhesive film on the front and back, and express with the arithmetic mean value (kPa) of all measured values

10. Test report

the test report includes the following contents:

a) the number of this national standard

b) sample type and specification

c) standards used in the test

d) atmospheric conditions of the test site

e) the name and model of the tester used, and the clamping force used

f) the average value of the bursting resistance of the front and back sides of the paperboard, with three significant figures retained

g) test date, place, test personnel, etc

statement: This article is reprinted. The purpose of publishing this article is to transmit market information more widely. The content of this article is for reference only. The copyright of this website article belongs to the original author and the original source. The content is the author's personal views, which does not mean that this website agrees with his views and is responsible for its authenticity. This website only provides reference and does not constitute any investment and application suggestions. Some articles on this website are reprinted and are not used for any commercial purposes. We have notified the author and source as much as possible. If there is any missing or inappropriate information, please contact us in time, and we will correct or delete the relevant content immediately according to the requirements of the copyright owner. This website has the final right to interpret this statement